Optical Properties of CIGS Films as Deposition Conditions of Mo Back Contact

MO 배면전극의 제조조건이 CIGS 박막의 광특성에 미치는 영향

  • Published : 2001.07.18

Abstract

Bi-layer Mo films were deposited on sodalime glass substrates using DC magnetron sputtering. As the gas pressure and power density, the resistivity varied from $1.5{\times}10^{-5}$ to $4.97{\times}10^{-4}{\Omega}{\cdot}cm$. Furthermore, stress direction yielded compressive-to-tensile transition stress curves. The microstructure of the compressive stress films which had poor adhesion consists of tightly packed columns, but of the tensile-stressed films had less dense structure. Under all gas pressure conditions, Mo films exhibited distinctly increasing optical reflection with decreasing gas pressure. The expansion of (110) peak width with the gas pressure meant the worse crystalline growth. Also, The highest efficiency was 15.2% on 0.2 $cm^2$. The fill factor, open circuit voltage and short circuit current were 63 %, 570 mV and 42.6 mA/$cm^2$ respectively.