초록
It was studied to prepare high temperature heating elements using molybdenum disilicide($MoSi_2$). Molybdenum disilicide is widely used as material for manufacturing high temperature heating elements. $MoSi_2$ heating elements could be used at 1700-1900$^{\circ}C$. However, it is relatively expensive, and its demand depends on import. $MoSi_2$ powders was mixed with 4-5wt% of montmorillonites type bentonite as plasticizer and a small amount of $Si_3N_4$, $ThO_2$, and B as additives to prepare specimen of heating elements. Then, it was extruded, dried, sintered and machined followed by heating test. Effects of sintering conditions and amount of additives were investigated, It was sintered effectively at 1,350$^{\circ}C$ for five hours. Electrical resistivity was decreased with increasing of sintering temperature and time, and related with apparent density of the specimens. It was linealy decreased with increasing of sintered density. The heating elements thus prepared was stable at 1700$^{\circ}C$ and the physical properties such as specific electrical resistivity, hardness, apparent density, thermal expansion coefficient, and bending strength were almost identical with those of commercial heating elements.