초록
Recently, the ceramics of high permittivity are applied to DRAM and FRAM. In this study, (Ba, Sr)$TiO_3$ (BST) ceramics thin films were prepared by Sol-Gel method. BST solution was made and spin-coated on Pt/$SiO_2$/Si substrate at 4000 [rpm] for 10 seconds. Coated specimens were dried at $150[^{\circ}C]$ for 5 minutes. Coating process was repeated 3 times and then sintered at $750[^{\circ}C]$ for 30 minutes. Each specimen was analyzed structure and electrical characteristics by Fractal Process. Thickness of BST ceramics thin films are about $2000{\AA}$. Dielectric constant and loss of thin films was little decreased at 1[KHz] - 1[MHz]. Dielectric constant and loss to frequency were 250 and 0.02 in BST3. The property of leakage current as the realation between the current and the voltage was that change of the leakage current was stable when the applied voltage was 0~3[V].