Spectrum analysis of acoustic Barkhausen noise on neutron irradiated material

In relation to a non-destructive evaluation of irradiation damage of micro-structure of interstitial, void and dislocation, the changes in the hysteresis loop and Barkhausen noise amplitude and the harmonics frequency due to neutron irradiation were measured and evaluated. The Mn-Mo-Ni low alloy steel of reactor pressure vessel was irradiated to a neutron fluence of $2.3\times10^{19}n/cm^2$ $(E\ge1MeV)$ at $288^{\circ}C.$The saturation magnetization of neutron irradiated metal did not change. Neutron irradiation caused the coercivity to increase, whereas susceptibility to decrease. The amplitude of Barkhausen noise parameters associated with the domain wall motion were decreased by neutron irradiation. The spectrum of Barkhausen noise was analyzed with an applied frequency of 4Hz and 8Hz, and a sampling time of 50 $\mu$ sec and 20 $\mu$ sec. The harmonic frequency of Joule effect shows 4Hz, 8Hz, 12Hz and 16Hz reflected from an unirradiated specimen. On the contrary, the harmonic frequency disappeared for the irradiated specimen. Harmonic frequency of induced voltage of sinusoidal magnetic field And Spectrum of Barkhausen noise on material is determined.