Abstract
The piezoelectric properties and the doping effect of N $b_2$ $O_{5}$ and Mn $O_2$for 0.95PbZ $r_{x}$ $Ti_{x}$ $O_3$+0.05Pb(M $n_{0.42}$ $W_{0.26}$S $b_{0.32}$) $O_3$ compositions have been investigated. In the composition of 0.95PbZ $r_{0.54}$ $Ti_{0.46}$ $O_3$+0.05Pb(M $n_{0.42}$ $W_{0.26}$S $b_{0.32}$) $O_3$the Values Of $k_{p}$ find and $\varepsilon$$_{33}$ $^{T}$ are maximized, but $Q_{m}$ Was minimized ( $k_{p}$ =0.51, $Q_{m}$ =1750). The grain size was suppressed and the uniformity of grain was improved with doping concentration of N $b_2$ $O_{5}$ for 0.95PbZ $r_{0.54}$ $Ti_{0.46}$ $O_3$+0.005Pb(M $n_{0.42}$ $W_{0.26}$S $b_{0.32}$) $O_3$sample. The values of $k_{p}$ increased and the values of $Q_{m}$ slightly decreased when 0.5 wt% of N $b_2$ $O_{5}$ is doped. And the values of $k_{p}$ was the same formation of the N $b_2$ $O_{5}$ dopant when 0.5 wt% of M $n_2$ $O_{5}$ is doped. But the values of $Q_{m}$ was deeply decreased when 0.5 wt% of Mn $O_2$is doped. As a experiment results under high electric field driving, this piezoelectric ceramics are very stable. Conclusively, piezoelectric ceramic compsiton investigated at this paper is suitable for application to high power piezoelectric devices.. devices..ices.. devices..