Fabrication and Characterization of BSCCO System High-Temperature Superconductor Using Centrifugal Forming Process

원심성형법을 이용한 BSCCO계 고온초전도체 제조 및 특성 분석

High-temperature superconductor of Bi-2212 system was fabricated by CFP(centrifugal forming process). To make a uniform specimen slurry was prepared in the ratio of 7:3(powder:binder) and ball milled for 24 hours. Milled slurry was charged into a rotating mold with 450 rpm and dried at room temperature. Then the specimen was performed binder burn-out at 35$0^{\circ}C$ and heated for partial melting to 86$0^{\circ}C$. XRD analysis of most specimens were shown 2212 phase and observed a local plate shaped microstructure with a well aligned c-axis direction from SEM images. T$_{c}$(Critical temperature) of Bi-2212 was 64K.K.