Abstract
The dynamic recrystallization (DRX) of medium carbon steels (SCM 440 and POSMA45) was studied with torsion test in the temperature range of $900-1100^{\circ}C$ and the strain rate range of $5.0x10^{-2}\;-\;5.0x10^0/sec$. To establish the quantitative equations for DRX, the evolution of flow stress curve with strain was analyzed. The critical strain (${\varepsilon}_c$) and strain for maximum softening rate ( ${\varepsilon}^{*}$) could be confirmed by the analysis of work hardening rate ($d{\sigma}/d{\varepsilon}\;=\; \theta$). The volume fraction of dynamic recrystallization ($X_{DRX}$) as a function of processing variables, such as strain rate ( $\dot{\varepsilon}$ ), temperature (T), and strain ( $\varepsilon$ ) were established using the ${\varepsilon}_c$ and ${\varepsilon}^{*}$. For the exact prediction, the ${\varepsilon}_c$, ${\varepsilon}^{*}$ and Avrami' exponent (m') were quantitatively expressed by dimensionless parameter, Z/A respectively. The transformation-effective strain-temperature curve for DRX could be composed. It was found that the calculated results were agreed with the experimental data for the steels at any deformation conditions.