The Cathodoluminance Properties of $Y_2SiO_5$:Ce Blue Phosphor with Surface Coatings

$Y_2SiO_5$:Ce 청색 형광체의 표면 코팅에 따른 음극선 발광특성

  • Published : 1999.11.01

Abstract

$Y_2SiO_5$:Ce was considered as blue phosphor for field emission display because it had an excellent resistance against brightness saturation. But unfortunately It hadn't a sufficient brightness to be applied to FED. In this experiment It-$In_2O_3$, MgO and $SiO_2$ were coated onto $Y_2SiO_5$:Ce phosphor in order to improve the cathodoluminance(CL properties. The coating structures were identified to be the crystalline phases of $In_2O_3$ and MgO respectively. They had fine particle-like shape and were distributed on the surface of $Y_2SiO_5$:Ce phosphor. It was found that the CL efficiency of $Y_2SiO_5$:Ce phosphors were decreased after coatings with In20:j and MgO in voltage range from 500 V to 5 kV. But the brightness of $Y_2SiO_5$:Ce phosphor was increased after coating of 5 0 2 . And also the aging test showed that $In_2O_3$ coating improved the life time of $Y_2SiO_5$:Ce phosphor.