Microstructure of Laser Surface Melted Ni-Base Alloy 600 after Heat Treatment

A study of treatment effects on laser surface melted Ni-base alloy 600, especially on precipitation behavior ad chemical composition changes on the grain boundary were conducted with microscopic equipments. Long-term aging treatment at 40$0^{\circ}C$ caused no considerable effects on the grain boundary properties. Cr-rich M$_2$$_3$C$_{6}$ and Cr$_{7}$C$_3$ carbides were precipitated and the resultant Cr depletion below 12 wt pct on some high angle grain boundaries was occurred by heat treatment at $600^{\circ}C$ for 24 hours. These results can imply that the resistance of intergranular stress corrosion cracking of heat treated alloy 600 might not be changed considerably in comparion with the as-LSM one.e.e.