Properties of thermally stimulated current of PAAS thin film using spin coating method

Spin coating한 polyamic acid alkylamine salt(PAAS) 박막의 열자격 전류 특성

  • Lee, H.S. (Dept. of Electrical and Control Engineering, Hong-Ik Univ.) ;
  • Lee, S.Y. (Dept. of Electrical and Control Engineering, Hong-Ik Univ.) ;
  • Lee, W.J. (Dept. of Electronics, Kyungwon Technical Univ.) ;
  • Kim, T.W. (Dept. of Physics, Hong-Ik Uni) ;
  • Kang, D.Y. (Dept. of Electrical and Control Engineering, Hong-Ik Univ.)
  • 이호식 (홍익대학교 전기제어공학과) ;
  • 이승엽 (홍익대학교 전기제어공학과) ;
  • 이원재 (경원전문대학교 전자과) ;
  • 김태완 (홍익대학교 물리학과) ;
  • 강도열 (홍익대학교 전기제어공학과)
  • Published : 1996.07.22
Download PDF
⟨ Previous Next ⟩

Abstract

This paper describes the thermally stimulated current(TSC) of PAAS spin coated film and the electrical properties of pre TSC measurement and after TSC test specimens. The TSC measurement were performed from room temperature to about $280^{\circ}C$ and the temperature was increased by $5^{\circ}C/min$ automatically. It shows that two peaks of TSC are observed at about $50^{\circ}C$ and about $160^{\circ}C$. Result of this measurement indicate that one peak; $50^{\circ}C$ is from alkyl group; other peak at $160^{\circ}C$ is due to alkyl and C-O group of PAAS. Addition to larger peak at about $160^{\circ}C$ is due to dipolemoment of PAAS film. This result is proved by DSC measurement of PAAS film. The electrical properties of pre and after TSC were measured by currant-voltage(l-V) characteristics. The current-voltage characteristics after TSC specimens are increased the conductivity. The electrical properties of pre-after TSC measurement specimen is in the middle of imidization of PAAS. Because of this result a thermal imidization was performed at $300^{\circ}C$ for 1 hour.