Abstract
The cubic (zinc blende) CdSe eppilayers were grown on GaAs(100) substrates by electron beam (e-beam) evapporation technique. X-ray scans with copper $K\alpha$ radiation indicate that the CdSe eppilayers are zinc blende. The lattice pparameter obtained from the (400) reflection is 6.077$\AA$, which is in excellent agreement with the value repported in the literature for zinc blende CdSe. The orientation of as-grown CdSe eppilayer is determined by electron channeling ppatterns(ECpp). The crystallinity of heteroeppitaxial CdSe layers were investigated based on the double crystal x-ray rocking curve(DCRC). The deppendence of the rocking curve width on layer thickness was studied. The FWHM(full width at half maximum) of CdSe eppilayers grown on GaAs(100) substrates is decreasing with increasing eppilayer thickness. The carrier concentration and mobility of the as-grown eppilayers deduced Hall data by van der ppauw method, are about 7$\times$1017 cm-3 and 2$\times$102 $\textrm{cm}^2$ / sec at room tempperature, resppectively. The energy gapp was determinded from the pphotocurrent sppectrum. In pphotocurrent sppectrum of a 1-${\mu}{\textrm}{m}$-thick CdSe eppilayer at 30K, the ppeak at 1.746 eV is due to the free exciton of cubic CdSe. In summary, We have shown that eppilayers of zinc blende CdSe can be grown on GaAs(100) substrates by e-beam, desppite the large mismatch between eppilayer and substrate, as well as the natural ppreference for CdSe to form in the wurtzite structure.