Formation ani Magnetic Properties of Iron-Nitrides due to Mechanical Alloying in $NH_3$ gas Atomosphere

The nitrification of pure iron powders is found to occur even at room temperature by high energy ball milling in $NH_3$ gas atmosphere. The powders of metastable iron nitrides ($0<at.%N{\le}23.3$) thus produced are identified as the super-saturated bee structure for the N content below 14.9 at.%N and the high temperature phase of the hcp structure above 19.4 at.%N. The atomic volume of Fe in the bcc phase is found to be smaller than that of the N-martensite reported in the literature. Magnetization at room temperature gradually decreases with increasing the N concentration in contrast to the enhancement reported for the bet nitrides. Neutron diffraction experiment also provide detailed information about the local structure surrounding the nitrogen atom. The coordination number of Fe atom around a nitrogen atom for the iron nitride containing 9.5 at.%N turns out to be 3.9 atoms.