GaP 산화막 특성에 관하여

On the Characteristics of Oxide Film on Gap

  • 발행 : 1988.11.25

초록

The native oxide films were thermally and anodically formed on the n-GaP substrates grown by SSD method and measured this oxide thickness and the chemical composition and the electrical properties with formation condition. The chemical composition of themally oxidized GaP film was composed of mostly $GaPO_4$ at temperature below $800^{\circ}C$ and mostly $\beta-Ga_{2}O_{3}$ above $800^{\circ}C$. But The chemical composition of anodically oxidized GaPfilm was composed of the mixture of $Ga_{2}O_{3}$ and $P_{2}O_{5}$. The barrier height of Al/oxide/n-Gap which was formed at $700^{\circ}C$ by thermal oxidation method were 1.10eV, 1.03eV in Current-Voltage measurement. Interface charge density were $4{\times}10^{12}q(C/cm^2)$ and $3{\times}10^{12}q(C/cm^2)$ in Capacitance-Voltage measurement respectively.