Abstract
Transparent CdS films with low electrical restivity on glass substrates were prepared by coating a CdS slurry which contained 10 wt.% $CdCl_2$, and sintering in a nitrogen atmosphere at $600^{\circ}C$ for 2hr. All-polycrystalline CdS/CdTe solar cells were fabricated by coating CdTe slurries, which contained 1.0 or 4.5 wt.% $CdCl_2$, on the sintered CdS films and sintering at $700^{\circ}C$ for various periods of sintering. The spectral responses of the sintered CdS/CdTe solar cells were measured and compared with theoretically calculated quantum efficiency. The spectral responses of the sintered CdS/CdTe solar cells in the short-wavelength region decreases with-increasing sintering time. The poor response in this region is attributed to the existence of the Cd-S-Te solid solution in the compositional junction. The decrease in the maximum response in the long-wavelength region as the sintering exceeds certain time appears to be caused by the increase in the depth of the buried homo junction and by the increase in the series resistance. The $CdCl_2$ in the CdTe layer during sintering enchances the interdiffusion of S, Te or donor impurities across the metallurgical Junction causing the formation of deeper n-p junction in the CdTe layer.